PPR ka pipe (Kopolimɛri Poliporopilɛni) ye bɔnsɔn sabanan ye- bɔnsɔn kɛrɛnkɛrɛnnin dɔ ye polipropilɛni piping kama, min be weele fana ko Polipropilɛn sifa 3nan. PPR Plastic Pipe be se ka homopolimɛri poliporopilɛni ka fiɲɛw bɔ, min be nɔɔ ɲuman to a ka nɔɔ ɲuman kan k’a sɔrɔ a be wagatijan kɛ ka to ka yɛlɛma. PPR Jii Pipe fana b’a to baara be se ka kɛ wagati jan kɔnɔ funteni ni kɔnɔna degun kelen kɔnɔ.
|
Sariya labatoli sariya:GB/T18742.2-2002 |
||||
|
Pipe seri |
S5(1.25MPa) |
S4(1.6MPa) |
S3.2(2.0MPa) |
S2.5(2.5MPa) |
|
Diamɛtiri min be kɛ kɛnɛma (mm) |
Kogow ka janya(mm) |
Kogow ka janya(mm) |
Kogow ka janya(mm) |
Kogow ka janya(mm) |
|
12 |
2.0 |
|||
|
16 |
2.0 |
2.2 |
2.7 |
|
|
20 |
2.0 |
2.3 |
2.8 |
3.4 |
|
25 |
2.3 |
2.8 |
3.5 |
4.2 |
|
32 |
2.9 |
3.6 |
4.4 |
5.4 |
|
40 |
3.7 |
4.5 |
5.5 |
6.7 |
|
50 |
4.6 |
5.6 |
6.9 |
8.3 |
|
63 |
5.8 |
7.1 |
8.6 |
10.5 |
|
75 |
6.8 |
8.4 |
10.3 |
12.5 |
|
90 |
8.2 |
10.1 |
12.3 |
15.0 |
|
110 |
10.0 |
12.3 |
15.1 |
18.3 |
|
125 |
11.4 |
14.0 |
17.1 |
20.8 |
|
140 |
12.7 |
15.7 |
19.2 |
23.3 |
|
160 |
14.6 |
17.9 |
21.9 |
26.6 |
PPR ka pipe fɛɛrɛ min be sɔrɔ kunnafoni dicogo la .
|
Minɛn |
ɲininkali |
Kɔrɔbɔliw cogoya |
||
|
Paramɛtiri |
Daman |
|||
|
buguri |
A ka dɔgɔ ni 1,5% ye wala min be bɛn . |
balansi funteni |
degere 600 |
|
|
ka funteni hakɛ min be se ka yɛlɛma |
-kirisitali PP-H |
Tpm1 A ka bon ni 145 degere Tpm2 ye min ka bon ni degere 160 ye wala min be bɛn degere 160 ma . |
Azɔti ji bɔli 50ml/min, kalaya/nɛnɛ hakɛ 10 degere /min,2 yɛlɛmaniw |
|
|
PP-B |
min ka bon ni degere 160 ye wala min be bɛn ɲɔgɔn ma . |
|||
|
PP-R |
A ka dɔgɔ ni degere 148 ye wala min be bɛn ɲɔgɔn ma . |
|||
|
-kirisitali PP-RCT |
Tpm1 hakɛ ka tɛmɛ 143 degere Tpm2 hakɛ kan ka tɛmɛ degere 157 kan walima min be bɛn . |
|||
|
Oxidasiyɔn wagati |
min ka bon ni miniti 20 ye wala min be bɛn n’o ye . |
balansi funteni |
degere 210 |
|
|
OIT degere 95 kɔ /1000h hydrostatique . |
min ka bon ni 16min ye wala min be bɛn n’a ye . |
|||
|
Pigment jɛnsɛnni |
A ka bon ni kalanso 3nan ye wala min be bɛn n’a ye. |
- |
||
|
Ɲɛyirali:A1,A2,A3 wala B . |
||||
|
Lolo yɛlɛmani |
-kirisitali PP-H |
A ka dɔgɔ ni 2% ye wala min be bɛn . |
enNi 8mm:1h . 8mm hakɛn16mm:2h . en16mm:4h |
(150±2) degere |
|
PP-B |
||||
|
PP-R |
(135±2) degere |
|||
|
-kirisitali PP-RCT |
||||
|
O dɛmɛ dɔrɔn lo be se ka kɛ ni yeelen ye . |
-kirisitali PP-H |
N’u y’u yɛrɛ sɛgɛsɛgɛ, o hakɛ ka dɔgɔ ni 10% ye . |
balansi funteni |
(23±2) degere |
|
PP-B |
||||
|
PP-R |
(0±2) degere |
|||
|
-kirisitali PP-RCT |
||||
|
A be se ka kɛ ko a ka ɲi ka kɛ i n’a fɔ yɔrɔ min be weele ko-. |
A ka dɔgɔ ni 0,5g/10min ye wala a be bɛn ni 20% yɛlɛmani ye ka bɔ PP componiment la . |
Kɔrɔbɔliw ka funteni hakɛ caya . |
230 degere 2.16kg |
|
|
Teliya basiginin be hydrostatique pressure ka fanga kɔrɔ . |
A ma tigɛ,o ji bɔli . |
Hidrostatiki yɔrɔ: -crisalline PP-H, PP-B, PP-R, -RCT ka kɔrɔbɔli . Kɔrɔbɔli hakɛ |
1.9MPa 1.4MPa 1.9MPa 2.6MPa degere 110 8760h |
|
|
Yeelen yɛlɛmani |
A ka dɔgɔ ni 0,2% ye wala min be bɛn . |
- |
||
|
Oxygène yɛlɛmani |
A ka dɔgɔ ni 0,1g/(m .3.d) |
|||
Kɛcogow
PP{{0}R tiyow tɛ ni pɔɔti nafaw dɔrɔn ye, i n’a fɔ nɔgɔya, fangaba, nɔgɔ, sɛgɛsɛgɛli -}.
1.Eco-son min ka ɲi ka kɛ: PP-R fɛn min be sɔrɔ poliolefin denbaya kɔnɔ, o be ni molekiliw ye minw be kɛ ni karbɔni ni hydrogène ye, ka saniyako baara lafiya.
2. Heat-seratɛri ani ka mɔgɔw lafili, o min b’a to a be kɛ fanga ye- ye min be se ka mara.
3. A ka nɔgɔ ani a be se ka la a la: homozene homogène de-melt be se ka kɛ sekɔndiw kɔnɔ, k’a sɔrɔ nɛgɛ min ka bon, nɛgɛ-}inbétables be se ka kɛ ka ɲɔgɔn minɛ ni nɛgɛ tiyow ni jii minanw ye, ka lakana ni lannaya sabati.
Ladilikanw
1.Duguw ka tiyo minw be kɛ boonw kɔnɔ, i n’a fɔ boon cɛmancɛw.
2. Ka boonw lɔ boonw kɔnɔ, i n’a fɔ: yɔrɔ minw ka dɔgɔ, kogow ka boonw ka kalaya ani u be yeelen bɔ.
3. Ka jii saniyalanw dilan cogo yira.
4. Sanfɛla (cɛmancɛ) fiɲɛ- ka ɲɛsin yɔrɔw ma.
Tagasogow: ppr jii tupe, Sinuwaw ka ppr jii tupe dilanbagaw, feerekɛlaw, izini .